Process for preparing cathode material for lithium batteries

ABSTRACT

The present invention relates to a novel process based on solid state thermal reaction for the preparation of cathode materials for lithium secondary batteries such as rocking chair and intercalated batteries.

FIELD OF THE INVENTION

[0001] The present invention relates to a novel process based on solid state thermal reaction for the preparation of cathode materials for lithium secondary batteries such as rocking chair and intercalated batteries.

BACKGROUND OF THE INVENTION

[0002] Lithium compounds such as lithium cobaltate (LiCoO₂) and lithium nickelate (LiNO₂) are widely used is cathode material for both lithium secondary cells and thin film micro-batteries due to its high reversibility to lithium ions, high cell capacity and less fading capacity over LiMn₂O₄.

[0003] In general lithium cobaltate materials are prepared by solid state thermal method and soft chemistry (like sol-gel) methods. The common materials for the preparation of this cathode lithium cobalate (LiCoO₂) are any one of the lithium salts viz. lithium nitrate or is lithium hydroxide, lithium acetate lithium carbonate with cobalt nitrate or cobalt oxide. Soft chemistry methods are mainly used to prepare the intercalation compounds at low temperatures and to reduce the particle size of the compounds. But the soft chemistry routes are multi-step procedures prolonged time for calcination and expensive. Prolonged heating time, mechanic grinding and intermittent cooling are major drawbacks of solid state thermal procedures. Other preparation methods are also available in literature for preparation of lithium cobaltate like pulsed laser deposition, sputtering and electrostatic spray deposition. Lithium nickelate is also useful as a cathode in lithium secondary cells of high voltage to replace present low energy density secondary storage cells. In the art it is known to prepare lithium nickelate by reacting lithium nitrate, or lithium hydroxides or any other lithium salts with lithium nitrates, acetates, hydroxides or sulphates by a sol-gel process at a temperature in the range of 350-500° C. However, separation of the final product requires several steps.

[0004] In the preparation of intercalation compounds, any one of the following disadvantages are observed in the above conventional procedures.

[0005] 1. Side reactions occur i.e., unexpected product.

[0006] 2. Unreacted material is left behind which acts as impurity.

[0007] 3. Partial reactions occur.

[0008] 4. Several steps are needed for preparation.

[0009] 5. Controlled conditions required.

[0010] 6. Long calcination time

[0011] 7. Nonhomogeneous reactant distribution during heating i.e., undesirable phases are formed.

[0012] Reference:

[0013] 1. “Synthesis and electrochemical properties of LiCoO₂ spinel cathodes”—S. Chol and A. Manthiram, Journal of the Electrochemical Society, Vol. 149(2) (2002) A162-166.

[0014] 2. “Fabrication of LiCoO₂ thin films by sol-gel method and characterization as positive electrodes for Li/LiCoO₂ cells”—M. N. Kim, H. Chung, Y. Park, J. Kim, J. Son, K. Park and H. Kim, Journal of Power Sources, Vol. 99(2001) 34-40.

[0015] 3. “High temperature combustion synthesis and electrochemical characterization of LiNiO₂, LiCoO₂ and LiMn₂O₄ for lithium ion secondary batteries”—M. M. Rao, C. Liebenow, M. Jayalakshmi, M. Wulff, U. Guth and F. Scholz, Journal of Solid State Electrochemistry, Vol. 5, Issue 5(2001) 348-354.

[0016] 4. “Lithiated cobaltates for lithium—ion batteries—Structure, morphology and electrochemistry of oxides grown by solid state reaction, wet chemistry and film deposition” C. Julien and S. Gastro-Garcia, Journal of Power Sources, Vol. 97-98 (2001) 290-293.

[0017] 5. “Electrochemical characterization of layered LiCoO₂ films prepared by electrostatic deposition”, Won-Sub Yoon, Sung-Ho Ban, Kyung-Keun Lee, Kwang-Bum Kim, Min Dyu Kim and Jay Min Lee, Journal of Power Sources, Vol. 97-98 (2001) 282-286.

[0018] 6. “Emulsion-derived lithium manganese oxide powder for positive electrodes in lithium ion batteries” Chung-Hsin Lu and Shang-Wei Lin, Journal of Power Sources, Vol. 93 (2001) 14-19.

[0019] 7. “Cobalt doped chromium oxides as cathode materials for secondary batteries for secondary lithium batteries” Dong Zhang, Branko N. Popov, Yury M. Poddrabansky, Pankaj Arora and Ralph E. White, Journal of Power Sources, Vol. 83 (1999)121-127.

[0020] 8. “Synthesis and electrochemical studies of spinel phase LiMn₂O₄ cathode materials prepared by the Pechini process”—W. Liu, G. C. Farrington, F. Chaput and B. Dunn Journal of the Electrochemical Society., Vol. 143, No.3(1996) 879-884.

[0021] 9. “Synthesis of electrochemical characterisation of LiMO₂ (M=Ni, Ni_(0.75)Co_(0.25)) for rechargeable lithium ion batteries”, Chun-Chieh Chang, N. Scarr and P. N Kumta, J. of Solid State Ionics, Vol 112, 329-344 (1998).

[0022] 10. “Structural and electrochemical properties of LiNi_(0.3)Co_(0.7)O₂ synthesized by different low temperature techniques”, C. Julien, S. S. Michael and S. Ziolkewicz, International Journal of Materials, Vol. 1(1999), 29-37

[0023] 11. “Synthesis and characterisation of LiCoNi_((-y))VO₄ lithium insertion materials”, S. Panero, P. Reale, F. Bonno, B. Serosati, M. Arrabito, D. Mazza and N. Pennazi, J. “of Solid State Ionics”, Vol. 128, 43-52, (2000)

[0024] 12. Preparation and characterisation of high density spherical LiNi_(0.8)CoO₂ “cathode material for lithium secondary batteries”, “Jierond Ying, Chunrong Wan, Changyin Jiang and Yangxing i, J. of Power Sources” Vol 99, (2001), 78-84

[0025] 13. “High temperature combustion synthesis and electrochemical characterisation of LiNiO₂, LiCoO₂ and LiMn₂O₄ “for lithium ion secondary batteries”, M. M. Rao, C. Liebnow, M. Jayalahshmi, M. Wulff, U. Guth and F. Scholz, J. of Solid State Electrochemistry”, Vol 5, Issue 5, 348-354 (2001)

OBJECTS OF THE INVENTION

[0026] The main object of the invention is to provide a process for the preparation of lithium cathode materials which overcomes the disadvantages of the prior art enumerated above.

[0027] It is another object of the invention, to provide a process for the manufacture of lithium cathode materials which does not involve the formation of side products.

[0028] It is a further object of the invention to provide a process for the manufacture of lithium cathode materials which does not result in impurities.

[0029] It is a firer object of the invention to provide a process for the manufacture of lithium cathode materials which does not involve a multiplicity of steps.

SUMMARY OF THE INVENTION

[0030] Accordingly the present invention relates to a solid state thermal process for the preparation of lithium cathode materials of the general formula LiMO₂ where M is Ni or Co comprising reacting solid lithium oxide (Li₂O) with metal compound selected from oxides and nitrates under controlled conditions.

[0031] In one embodiment of the invention, the metal oxide is Co₃O₄ and the Lithium oxide and the cobalt (II) oxide are mixed in stoichiometric condition.

[0032] In another embodiment of the invention, the reactants are heated at a temperature in the range of 450 to 750° C.

[0033] In a fisher embodiment of the invention the reactants are of analytical reagent grade.

[0034] In another embodiment of the invention, the metal nitrate is nickel nitrate,

[0035] In a further embodiment of the invention, urea or ammonium nitrate is added to the reaction mixture of lithium oxide and cobalt (II) oxide as self heat generating materials and ground well.

[0036] In yet another embodiment of the invention the ratio of Li₂O+Co₃O₄ mixture and urea or ammonium nitrate additive is 1:3.

[0037] In a further embodiment of the invention, the process comprises mixing solid lithium oxide and cobalt (II) oxide, mixing urea in the resultant mixture and grinding the final mixture, introducing the resultant mixture in a furnace and heating at a temperature in the range of 450 to 750° C. to obtain lithium cobaltate.

[0038] In one embodiment of the invention, the Li₂O is mixed with Co₃O₄ in the following preferred proportions Li₂O:Co₃O₄=0.16; 0.84 (for 1 gram)

[0039] In another embodiment of the invention, the process comprises mixing solid lithium oxide and nickel nitrate and heating to a temperature in the range of 450 to 750° C. to obtain lithium nickelate.

[0040] In another embodiment of the invention, the lithium oxide and nickel nitrate are mixed in the, ratio of 1;2.

DETAILED DESCRIPTION OF THE INVENTION

[0041] The present invention provides a simple single step reaction for the preparation of cathode materials for lithium secondary cells such as lithium cobaltate and lithium nickelate. The process comprises solid state mixing of the lithium oxide with the corresponding metal compound and heating with or without the addition of urea. The preferred temperature range for the heating which is carried out continuously in a furnace is 500 to 750° C. for a period of about 8 hours. The products formed were examined by X-ray diffraction for confirmation. The following reaction occurs during the thermal process when the metal is cobalt.

3Li₂O+2Co₃O₄+(O)→6LiCoO₂

[0042] Li₂O is mixed with Co₃O₄ in the following desired proportions Li₂O:Co₃O₄=0.16; 0.84 (for 1 gram). It is preferred that the reaction takes place in an electric fie. The materials used are all in the solid state.

[0043] Preparation of LiCoO₂ Through Solid State Thermal Reaction:

[0044] (A) Li₂O solid state material is allowed to react with solid Co₃O₄ under controlled conditions at modern temperature which yields fairly very good sample of spinel structure used as a very good intercalating cathode. Stoichiometric amount of Pure AR sample of Co₃O₄ is mixed with pure AR sample of Li₂O in the cationic ratio of Li:Co is (1:1) for the preparation of LiCoO₂. This mixture is thoroughly mixed with urea in the ratio of 1:3 (mixture: urea). This uniform mixture was preheated at 300° C. for 3 hours. In order to obtain a better homogeneous mixture, this mixture is ground well with double distilled water free ethylene carbonate (EC). This mixture was again heated to 700° C. for 5 hours continuously to yield lithium cobaltate (LiCoO₂) which is evidenced by X-ray analysis (FIG. 1a).

[0045] (B) Li₂O solid state material is allowed to react with solid Co₃O₄ under controlled conditions at moderate temperature which yields fairly very good sample of spinel structure useful as a very good intercalating cathode. Stoichiometric amount of Pure AR sample of Co_(3O) ₄ and pure AR sample of Li₂O in the cationic ratio of Li:Co is (1:1) for the preparation of LiCoO₂. This mixture is thoroughly mixed with ammonium nitrate in the ratio of 1:3 (mixture: a onium nitrate). This uniform mixture was preheated at 300° C. for 3 hours. In order to obtain a better homogeneous mixture, this mixture is ground well with double distilled water free ethylene carbonate (EC). Again this mixture was heated to 700° C. for 5 hours continuously to yield lithium cobaltate (LiCoO₂) which is evidenced by X-ray analysis (FIG. 1b).

[0046] The following reaction occurs during the thermal process.

3Li₂O+2Co₃O₄+(O)→6LiCoO₂

[0047] Preparation of LiNiO₂ Through Solid State Thermal Reaction:

[0048] (A) Li₂O solid state material is allowed to react with solid Ni(NO₃)₂ under controlled conditions at moderate temperature which yields fairly very good sample of spinel structure useful as a very good intercalating cathode. Pure AR sample of Ni(NO₃)₂ is mixed with pure AR sample of Li₂O in the ratio of 2:1 such that an uniform mixture is formed. This mixture when heated to 600° C. for 12 hours continuously yields lithium nickelate LiNiO₂ which is evidenced by X-ray analysis (FIG. 2).

[0049] (B) Li₂O solid state material is allowed to react with solid Ni(NO₃)₂ under controlled conditions at moderate temperatures which yields fairly very good sample of spinel structure useful as a very good intercalating cathode. Ni(NO₃)₂ is mixed with lithium salt Li₂O in the ratio of 2:1 such that an uniform mixture is formed. The Sure when heated continuously at a temperature of about 500° C. yields lithium nickelate confirmed by X-rays analysis (FIG. 2).

[0050] The following reaction occurs during the thermal process.

Li₂O+Ni(NO₃)₂+(O)→2LiNiO₂+4NO₂+2O₂

[0051] The following examples are given by way of illustration and therefore should not be construed to limit the scope of the present invention.

EXAMPLE-1

[0052] AR pure dry Li₂O is mixed with AR pure dry Co₃O₄ in the ratio of 0.16:0.84 in a pestle and mortar arrangement and then the mixture is further mixed with 3 times the weight of urea and then introduced in an electric furnace. This mixture was heated first for 3 hours at 300° C. and then again heated at 700° C. for 5 hours. Components Compositions Li₂O 0.16 g* Co₃O₄ 0.84 g* Urea 3.00 g  Pre heating temperature 300° C. Final temperature 700° C. Time 8 hours Particle size of the product 10-20 μm Nature of the product Black Efficiency of the process >90%

EXAMPLE-2

[0053] Pure dry AR Li2O is mixed with pure dry AR Co₃O₄ in the molar ratio of 0.16:0.84 in a pestle and mortar arrangement and then the mix is further mixed with 3 times the weight of ammonium nitrate. The final mixture was heated first for 3 hours at 300° C. and then heated at 700° C. for 5 hours. Components Compositions Li₂O 0.16 g* Co₃O₄ 0.84 g* Ammonium nitrate 3.00 g  Pre heating temperature 300° C. Final temperature 700° C. Time 8 hours Particle size of the product 10-20 μm Nature of the product Black Efficiency of the process >90%

EXAMPLE-3

[0054] AR pure dry Li₂O is mixed with AR pure dry Ni(NO₃)₂ in the molar ratio of 1:2 in a pestle and mortar arrangement and the mix is then introduced in an electric furnace. This mixture is heated for 12 hours at 600° C. Components Compositions Li₂O 0.5 g Ni(NO₃)₂ 1.0 g Pre heating temperature 100° C. Final temperature 600° C. Time 12 hours Particle size of the product 10-20 μm Nature of the product Black Efficiency of the process >80%

EXAMPLE-4

[0055] Pure dry AR Li₂O is mixed with pure dry AR Ni(NO₃)₂ in the molar ratio of 1:2 in a pestle and mortar arrangement and the mix is then introduced into an electric furnace and heated for 12 hours continuously at 500° C. Components Compositions Li₂O 0.5 g Ni(NO₃)₂ 1.0 g Pre heating temperature 100° C. Final temperature* 500° C. Time 12 hours Particle size of the product 10-20 μm Nature of the product Black Efficiency of the process >80%

[0056] *in LiNiO₂, AR spectra at 500° C. The peak at 20=68° is not well formed and the peak at 20=31° is present when compared to the standard.

[0057] The Main Advantages of the Present Invention Are

[0058] 1. It is a single step solid state thermal process

[0059] 2. Li₂O is used to react with Co₃O₄ to form LiCoO₂ and with Ni(NO₃)₂ to obtain LiNiO₂ of high capacity cathode for intercalation

[0060] 3. Heating time is considerably less, and hence considerable-heating time can be saved. 

We claim
 1. A solid state thermal process for the preparation of lithium cathode materials of the general formula LiMO₂ where M is Ni or Co comprising reacting solid lithium oxide (Li₂O) with metal compound selected from oxides and nitrates under controlled conditions.
 2. A process as claimed in claim 1 wherein the metal oxide is Co₃O₄ and the Lithium oxide and the cobalt (II) oxide are mixed in stoichiometric condition.
 3. A process as claimed in claim 1 wherein the reactants are heated at a temperature in the range of 450 to 750° C.
 4. A process as claimed in claim 1 wherein the reactants are of analytical reagent grade.
 5. A process as claimed in claim 1 wherein the metal nitrate is nickel nitrate.
 6. A process as claimed in claim 1 wherein urea or ammonium nitrate is added to the reaction mixture of lithium oxide and cobalt (II) oxide as self heat generating materials and the mixture ground well.
 7. A process as claimed in claim 6 wherein the ratio of Li₂O+Co₃O₄ mite and urea or ammonium nitrate additive is 1:3.
 8. A process as claimed in claim 1 wherein the process comprises mixing solid lithium oxide and cobalt (II) oxide, mixing urea in the resultant mixture and winding the final mixture, introducing the resultant mixture in a furnace and heating at a temperature in the range of 450 to 750° C. to obtain lithium cobaltate.
 9. A process as claimed in claim 8 wherein the Li₂O is mixed with Co₃O₄ in the following proportion Li₂O:Co₃O₄=0.16:0.84 (per gram).
 10. A process as claimed in claim 1 wherein the process comprises mixing solid lithium oxide and nickel nitrate and heating to a temperature in the range of 450 to 750° C. to obtain lithium nickelate.
 11. A process as claimed in claim 11 wherein the lithium oxide and nickel nitrate are mixed in the molar ratio of 1:2.
 12. A process as claimed in claim 1 wherein the process is a single step process.
 13. A process as claimed in claim 1 wherein no side reactions occur. 